|Year : 2020 | Volume
| Issue : 5 | Page : 554-559
Comparative study on fracture resistance of endodontically treated tooth in relation to variable ferrule heights using custom-made and prefabricated post and core: An in vitro study
Singaravelu Suresh Kumar, Mani Viswanathan, Krishnan Rajkumar, Chinnappan Marudhamani, V Shanmugam Rajaganeshan, K Antony Biju
KSR Institute of Dental Science and Research, Thiruchengodu, Tamil Nadu, India
|Date of Submission||10-Feb-2020|
|Date of Decision||13-Mar-2020|
|Date of Acceptance||02-Apr-2020|
|Date of Web Publication||28-Aug-2020|
Singaravelu Suresh Kumar
KSR Institute of Dental Science and Research, Thiruchengode, Namakkal, Tamil Nadu.
Source of Support: None, Conflict of Interest: None
| Abstract|| |
Introduction: Endodontically treated teeth have significantly differentphysical properties compared to vital teeth. To ensure functional longevity,endodontically treated teeth must have at least 5 mm of tooth structure coronalto the crestal bone, 2 mm of coronal tooth structure incisal to the preparationfinish line are necessary to ensure functional integrity. Aim and Objectives: To evaluate fracture resistance of endodontically treated teeth restored withcustom cast post, custom cast post with variable ferrule height and teethwithout ferrule, prefabricated post with variable ferrule height and teethwithout ferrule. To compare fracture resistance of teeth restored with customcast post and prefabricated post with variable ferrule heights. Materials and Methods: Methodology includes selection of teeth, root canal preparation,post space preparation, grouping of samples, Group A�custom cast post andcore with sub groups of variable ferrule height, pattern fabrication, Group A- pattern fabrication for customized cast post. Group B�pattern fabricationfor prefabricated post and core, investing and casting, cementation, custommade acrylic jig preparation, testing of specimens. Results: The differencein the fracture load between the samples of Group A was highly significantat the 0.001 level. Subgroup A4 had highest fracture resistance while GroupA, possessed the least fracture resistance. Subgroups A2, A3 had fractureresistance value intermediate between A1, A4. Conclusion: Increasing theferrule height significantly increases (P < 0.001) the fracture resistance ofendodontically treated teeth restored with both custom made cast post andcore and prefabricated post with metal core. Comparatively the custom madecast post and core with variable ferrule height, especially 2 mm ferrule showedsignificant fracture resistance than prefabricated post with metal core. Thepresence of 2 mm ferrule height significantly increases (P < 0.001).
Keywords: Custom-made cast post, custom-made jig, endodontically treated teeth, ferrule, prefabricated cast post
|How to cite this article:|
Kumar SS, Viswanathan M, Rajkumar K, Marudhamani C, Rajaganeshan V S, Biju K A. Comparative study on fracture resistance of endodontically treated tooth in relation to variable ferrule heights using custom-made and prefabricated post and core: An in vitro study. J Pharm Bioall Sci 2020;12, Suppl S1:554-9
|How to cite this URL:|
Kumar SS, Viswanathan M, Rajkumar K, Marudhamani C, Rajaganeshan V S, Biju K A. Comparative study on fracture resistance of endodontically treated tooth in relation to variable ferrule heights using custom-made and prefabricated post and core: An in vitro study. J Pharm Bioall Sci [serial online] 2020 [cited 2020 Sep 19];12, Suppl S1:554-9. Available from: http://www.jpbsonline.org/text.asp?2020/12/5/554/292845
| Introduction|| |
The success achieved with aesthetic restoration has resulted in increased patient demands for these treatments. Consequently, there has been a significant increase in the use of all ceramic crowns and endodontic post with core. Endodontically treated teeth need to be protected, because there is a risk of fracture, particularly in the cervical region, which is. Endodontically treated teeth have significantly different strength compared to vital teeth. To ensure the functional longevity, endodontically treated teeth must have at least 5 mm of tooth structure coronal to crestal bone, 3 mm needed to maintain a healthy soft tissue complex, and 2 mm of coronal tooth structure incisal to the preparation finish line are necessary to ensure the functional integrity. It is generally accepted that restorative strategy to include to design a ferrule in tooth preparation when restoring endodontically treated tooth with a post and core and then restoring with crown. It has been stated that ferrule design improves the resistance to dynamic occlusal loading, maintains the integrity of the artificial crown retainer, and reduces the potential of concentration of stress at the junction of post with core. Furthermore, the ferrule effect reduces the wedging of tapered posts or bending forces during post insertion and helps to improve the marginal integrity of the fixed partial dentures. The effectiveness of ferrule has been evaluated by a variety of methods, including fracture testing, fatigue testing, and photoelastic analysis.,,,, Hence, it is decided to conduct a study on different ferrule heights ranging from 0, 1, 1.5, and 2 mm in a natural tooth as an in vitro study with the following aims, to evaluate the fracture resistance of endodontically treated teeth restored with custom-made cast post and prefabricated post with metal core, to evaluate and compare the fracture resistance of teeth restored with custom-made cast post and prefabricated post with variable ferrule height and teeth without ferrule, and to compare fracture resistance of teeth restored with custom-made cast post and prefabricated post with variable ferrule heights.
| Materials and Methods|| |
This study was performed to evaluate the influence of variable ferrule height fracture resistance of endodontically treated teeth restored with custom-made cast post and prefabricated post with core. Methodology includes, selection of teeth, root canal preparation, and post space preparation. Samples are grouped accordingly as follows: Group A—custom-made cast post and core with subgroups of variable ferrule height [Figure 1]A–E (A1 = 0 mm, A2 = 1 mm, A3 = 1.5 mm, and A4 = 2 mm) and Group B—prefabricated post with core, subgroups are named as follows: variable ferrule height (B1 = 0 mm, B2 = 1 mm, B3 = 1.5 mm, and B4 = 2 mm). Group B, pattern fabrication for prefabricated post and core, investing and casting, cementation, acrylic block preparation, preparation of metal core for receiving porcelain fused metal crown, custom-made acrylic jig preparation.
After post space preparation, 40 teeth were grouped into two major groups of custom-made cast post with core (Group A) and prefabricated post with metal core (Group B) [Figure 2]. Both Groups A and B are further divided into four subgroups with variable ferrule height.
|Figure 2: (A) No ferrule, (B) 1 mm ferrule, (C) 1.5 mm ferrule, (D) 2 mm ferrule|
Click here to view
For subgroups A1 and B1 [Figure 3]A (0 mm/no ferrule), the coronal aspects of the teeth were removed at the cementoenamel junction perpendicular to the long axis of the tooth by using high-speed handpiece with flat end tapering diamond. No coronal dentin was remaining.
For the subgroups [Figure 3B] A2 and B2 (1 mm), coronal tooth structure was reduced to a flat plane at a height of 1 mm coronal to cementoenamel junction circumferentially. Ferrule height was standardized by customized probe having measurement of 0.5, 1.0, 1.5, and 2.0 mm.
For the subgroups [Figure 3C] A3 and B3 (1.5 mm), the coronal tooth structure was reduced to a flat plane at a height of 1.5 mm coronal to cementoenamel junction circumferentially, the ferrule height was standardized by customized probe having the measurement of 0.5, 1.0, 1.5, and 2.0 mm. For the subgroups A4 and B4 [Figure 3D] (2 mm), coronal tooth structure was reduced to a flat plane at a height of 2 mm coronal to cementoenamel junction circumferentially, ferrule height was standardized by customized probe having the measurement of 0.5, 1.0, 1.5, and 2.0 mm. Custom-made acrylic jig preparation is shown in [Figure 4]. A custom-made jig, which would fit exactly in retaining the arm of universal testing machine, was made from the rectangular block of acrylic. This was designed to hold the samples at 135° to the proposed loading. It was to orient all the specimens in the universal testing machine at 135° angulation.
|Figure 4: (A) Group A—different ferrule prefabricated post, (B) prefabricated post and custom made post with core, (C) Group B— wax pattern for custom post, (D) Group A Acrylic block and post with core, (E) Group B Acrylic block and post with core, (F) testing of specimen|
Click here to view
Testing of specimens
Each specimen was placed in custom-made apparatus that allowed the specimens to be positioned at 45° to the buccal/lingual axis. Specimens were subjected to loading at this orientation in a universal testing machine. The load was measured in Newton (N). Each specimen was embedded in a self-cured acrylic resin block from 2.0 mm apical to the margins of a porcelain-fused metal crown, and then loaded at 135° from the long axis in a universal testing machine at a crosshead speed of 1.0 mm/min until fracture. Static loading tests were performed on each specimen until failure (crack without a complete fracture).
| Results|| |
This study was conducted to evaluate the fracture resistance of endodontically treated teeth restored with prefabricated post and custom-made cast post with variable ferrule heights. A total number of 40 samples were made. The samples were divided into two main Groups of A and B. These groups were further divided into eight subgroups of A1, A2, A3, and A4 and B1, B2, B3, and B4 of five samples each. All the samples were subjected to fracture test at particular load with universal testing machine. The load was recorded in Newton (N). The basic data of the results of this study are shown in [Table 1] and [Table 2]. The fracture loads of custom-made cast post with core (Group A) are given in [Table 1]. Fracture resistance of subgroup A4 is the highest (2 mm ferrule). Subgroup A1 (0 mm ferrule) has the least fracture resistance, with A2 and A3 in between these two. The fracture loads of prefabricated (Group B) post and core are given in [Table 1]. Subgroup B1 show a lowest fracture resistance. Remaining subgroups (B1, B2, and B3) for fracture loads are in increasing order. Subgroup B4 has the highest fracture resistant, [Table 1] represents the mean fracture load of both groups A and B. The fracture load of Group A and Group B samples is subjected to the following test for statistical analysis.
|Table 1: Mean values, standard deviation, and results of the one-way analysis of variance and Tukey honestly significant difference test between Groups A and B|
Click here to view
- One-way analysis of variance (ANOVA): when the mean values of three or more independent groups have to be compared, then one-way ANOVA test is used for observations. In the one-way ANOVA, the observed variability is subdivided into two components: Variability of the observations within a group about the group mean and variability of group mean between groups about overall mean. In this study, one-way ANOVA was used to determine the statistical differences in the fracture load between the groups.
- Tukey honestly significant difference (HSD) test: a statistically significant one-way ANOVA only indicates that the population mean values are probably unequal. It does not pinpoint where the differences are, so to determine this, multiple comparison tests are carried out. In this study, significant difference was determined using ANOVA; the results of one-way ANOVA and Tukey HSD test are given in [Table 1]. Tukey grouping is given in alphabets. Groups arranged in alphabetical order denote decrease in fracture load, which is significant at 5% level [Table 1]. The difference in the fracture load between the samples of Group A was highly statistically significant at level of 0.001. Subgroup A4 had the highest fracture resistance, whereas subgroup A1 possessed the least fracture resistance. Subgroups A2 and A3 had fracture resistance value intermediate between A1 and A4. Differences were significant at a significant level of 0.050 [Table 2]. The differences in fracture load between Group A and Group B were compared by paired Student’s t test and was highly significant at the level of 0.001%. Subgroup B4 had the highest fracture resistance, whereas subgroup B1 possessed the least fracture resistance values. The subgroups B2 and B4 have fracture resistance in between B1 and B4. The differences were significant at a significant level of 0.050 [Table 2]. The differences in fracture load between Group A and Group B were compared by paired Student’s t test and were found to be highly significant at the level of 0.001%.
| Discussion|| |
Dentists frequently restore teeth that have been endodontically treated. Restoration of endodontically treated anterior teeth with weakened roots requires special attention because the aesthetics and functions of those teeth must be reconstructed. Post with core is a commonly advocated method to replace the lost coronal tooth structure and to provide retention and resistance of the final restoration. A number of materials are available for this purpose. Materials currently available for posts are cast alloys, prefabricated stainless steel alloys, prefabricated glass ceramic post, prefabricated carbon fiber post, and custom-made post produced intraorally by cast metal or composite. For better performance of the post, the dimension of the post and certain physical characteristics of materials, such as strength and modulus of elasticity, are important with respect to preservation and fracture strength of the tooth structure. Lyons and Baxendale observed that the mean force applied on a maxillary canine was 215N. In the presence of para-functional loading, this force increased to 254.8N and the maximum force was between 343 and 362.6N. In this study, the maximal force to induce fracture of teeth with a uniform 2 mm ferrule was 835.5N for custom-made cast post and 755.6N for prefabricated post with metal core. This observation leads to the conclusion that there is substantial benefit in providing a ferrule whenever possible. The result of this study indicates that the presence of remaining coronal tooth structure did influence the fracture resistance of tooth. The findings of this study are in agreement with Sorensen and Engelman, who found that 1 mm of remaining coronal tooth structure was able to resist compressive load. In another study, Sorensen and Engelman showed that 1 mm of remaining coronal tooth structure nearly doubled the fracture resistance of endodontically treated teeth. Libman and Nicholls suggested that to achieve the full benefits of ferrule effect it should be a minimum of 1.5 mm in height and have parallel dentinal walls, totally encircle the tooth, end on sound tooth structure, and avoid invasion of the attachment apparatus of the tooth. In this study and other authors [7, 13, 15] concurred that fracture resistance was for test specimens with. It was observed that both custom-made cast post and the prefabricated post with metal core in 2 mm ferrule presented significantly higher fracture resistance when compared to 0 mm and 1 mm ferrule groups. These findings could be attributed to the good strength and modulus of elasticity of nickel–chromium alloy and the ferrule height, which is good enough to allow the post core to hold the dentinal tubules together against the functional force encountered. Pareira et al. observed that teeth restored with prefabricated post with composite core with 2 mm ferrule showed significantly higher fracture resistance of 745.3N. This is due to larger amount of coronal tooth structure. The higher quantity of inorganic particles corresponds to the maximum resistance of compressive load, surface hardness, and wear resistance. Shillingburg et al. found when all tooth structures have been lost to the level of alveolar crest or beyond, because of either fracture or caries, the tooth cannot be satisfactorily restored without some extraordinary measure; even if a dowel core placed in tooth, root will remain susceptible to fracture unless the crown encircles the tooth apical to the core. The ferrule effect around the tooth protects it from fracture by dowel from within, in fact if tooth structure is lost “only” to the level of epithelial attachment, it may be desirable to permit access to enough tooth structure apical to the finish line to produce a ferrule effect. This study also confirms that the presence of ferrule of 1.5 mm and 2 mm reduces significantly fracture of root (P <0.001). Tan et al. observed that tooth with a nonuniform ferrule is more effective at resisting fracture than a tooth with no ferrule but not as effective as a tooth with a uniform 2 mm ferrule. The result of this study is in agreement with that of Tan et al. Pareira et al. showed that most common cause of failure when using a direct technique (prefabricated post with composite resin) fractured the restorative material, and when the cast post with core was used, the most common failure was the fracture of root. In this study, prefabricated post with metal core that covers the ferrule, commonly fractures at junction between cementoenamel junction and remaining coronal tooth structure. This investigation showed that roots restored by custom-made cast posts showed higher fracture force resistance than those restored by prefabricated post with metal core. Despite its lower resistance, the prefabricated posts may be appropriate because there were no root fractures. Thus, this study showed that increase in ferrule height increases fracture resistance of teeth samples restored with both custom-made cast post and prefabricated post with metal core and maximum fracture resistance attained at a ferrule height of 2 mm. The custom-made cast post showed more resistance against the fracture when compared to prefabricated post and core. From the results of this study, it is observed that the custom-made cast post showed more resistance against the fracture even though the fracture was noticed at root level in some samples. The prefabricated post though needs lesser force to fracture, the occurrence of root fracture is comparatively less. As this study was conducted as an in vitro study, it has got its own pitfalls, such as dry atmosphere and fatigue loading. Further modified studies may be helpful to assess more details about the ferrule effect.
| Conclusion|| |
Within the limitation of this study, it can be concluded that increasing ferrule height significantly increases (P < 0.001) the fracture resistance of endodontically treated teeth restored with both custom-made cast post and core and prefabricated post with metal core. Comparatively, the custom-made cast post and core with variable ferrule height, especially 2 mm ferrule height, was statistically significant (P <0.001) to the fracture resistance of endodontically treated teeth restored with both custom-made cast post with core and prefabricated post with metal core when compared with teeth without ferrule.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Newman MP, Yaman P, Dennison J, Rafter M, Billy E Fracture resistance of endodontically treated teeth restored with composite posts. J Prosthet Dent 2003;89:360-7.
Pierrisnard L, Bohin F, Renault P, Barquins M Coron-radicular reconstruction of pulpless teeth: a mechanical study using finite element analysis. J Prosthet Dent 2002;88:442-8.
Carter JM, Sorensen SE, Johnson RR, Teitelbaum RL, Levine MS Punch shear testing of extracted vital and endodontically treated teeth. J Biomech 1983;16:841-8.
Spear F When to restore, when to remove: the single debilitated tooth. Compend Contin Educ Dent 1999;20:316-28.
Dikabas I, Tanalp J, Ozel E, Kokcel T, Ersoy M Evaluation of different ferrule designs on the fracture resistance of endodontically treated maxillary central incisor incorporating fiber posts, composite cores and crown restorations. J Contemp Dent Pract 2007;8:62-9.
Barkhordar RA, Radke R, Abbasi J Effect of metal collars on resistance of endodontically treated teeth to root fracture. J Prosthet Dent 1989;61:676-8.
Milot P, Stein RS Root fracture in endodontically treated teeth related to post selection and crown design. J Prosthet Dent 1992;68:428-35.
Patel A, Gutteridge DL An in vitro
investigation of cast post and partial core design. J Dent 1996;24:281-7.
Saupe WA, Gluskin AH, Radke RA Jr. A comparative study of fracture resistance between morphologic dowel and cores and a resin-reinforced dowel system in the intraradicular restoration of structurally compromised roots. Quintessence Int 1996;27:483-91.
Tjan AH, Whang SB Resistance to root fracture of dowel channels with various thicknesses of buccal dentin walls. J Prosthet Dent 1985;53:496-500.
Hunt PR, Gogarnoiu D Evolution of post and core systems. J Esthet Dent 1996;8:74-83.
Lyons MF, Baxendale RH A preliminary electromyographic study of bite force and jaw-closing muscle fatigue in human subjects with advanced tooth wear. J Oral Rehabil 1990;17: 311-8.
Sorensen JA, Engelman MJ Ferrule design and fracture resistance of endodontically treated teeth. J Prosthet Dent 1990;63:529-36.
Libman WJ, Nicholls JI Load fatigue of teeth restored with cast posts and cores and complete crowns. Int J Prosthodont 1995;8:155-61.
Ichim I, Kuzmanovic DV, Love RM A finite element analysis of ferrule design on restoration resistance and distribution of stress within a root. Int Endod J 2006;39:443-52.
Pareira JR, Ornelas F, Conti RCR, do Valle AL Effect of a crown ferrule on the fracture resistance of endodontically treated teeth restored with prefabricated posts. J Prosthet Dent 2006;95:50-7.
Shillingburg HT, Hobo S, Whitsett LD, Jacobi R, Brackett SE Fundamentals of fixed prosthodontics. 3rd ed. Chicago, IL: Quintessence Publishing; 1997. p. 89.
Tan PL, Aquilino SA, Gratton DG, Stanford CM, Tan SC, Johnson WT, et al
. In vitro
fracture resistance of endodontically treated central incisors with varying ferrule heights and configurations. J Prosthet Dent 2005;93:331-6.
[Figure 1], [Figure 2], [Figure 3], [Figure 4]
[Table 1], [Table 2]