| ORIGINAL ARTICLE |
|
| Year : 2018 | Volume
: 10
| Issue : 1 | Page : 43-47 |
|
|
Initial response of human bone marrow–derived stem cells after contact with ultrahigh-molecular-weight polyethylene (UHMWPE) material: An in vitro study on cell viability and interleukin-6 expression
Iwan B Anwar1, Asep
Santoso1, Eko
Saputra2, Rifky
Ismail2, J
Jamari2, Emile
van der Heide3
1 Orthopaedic and Traumatology Department, Prof. Dr. R. Soeharso Orthopaedic Hospital, Surakarta, Indonesia
2 Laboratory for Engineering Design and Tribology, Department of Mechanical Engineering, Diponegoro University, Tembalang, Semarang, Indonesia
3 Laboratory for Surface Technology and Tribology, Faculty of Engineering Technology, University of Twente Drienerloolaan, Enschede, The Netherlands
| Date of Web Publication | 20-Mar-2018 |
Correspondence Address:
Dr. Iwan B Anwar
Orthopaedic and Traumatology Department, Prof. Dr. R. Soeharso Orthopaedic Hospital, Jl. A. Yani Pabelan, Surakarta 57162
Indonesia
 Source of Support: None, Conflict of Interest: None  | Check |
DOI: 10.4103/jpbs.JPBS_70_17
 Abstract | | |
Introduction: Ultrahigh-molecular-weight polyethylene (UHMWPE) is a thermoplastic polymer useful in biomaterial applications, especially in orthopedic field. Yet, little is known concerning its initial effect on human bone marrow stem cells (hBMSCs) after implantation. Materials and Methods: A cytotoxicity analysis was performed with a 3-(4,5-dimethylthiazol 2-yl)-2,5-diphenyltetrazolium assay after 24, 48, and 72h of incubation of hBMSC culture. Expression of interleukin-6 (IL-6) was measured using enzyme-linked immunosorbent assay. Cell viability was measured with Inhibitory concentration 50% (IC50) formula. Results: All treatment groups showed a cell viability of >50% ranging from 78% to >100%. Lower expression of IL-6 of hBMSC compared to control group was found in 48h of incubation period. Conclusion: hBMSC showed high cell viability after initial contact with UHMWPE material. Modulation of IL-6 expression was present at the initial stage as a response to foreign material.
Keywords: Cell viability, human stem cells, interleukin-6, UHMWPE
How to cite this article:
Anwar IB, Santoso A
, Saputra E
, Ismail R
, Jamari J
, van der Heide E
. Initial response of human bone marrow–derived stem cells after contact with ultrahigh-molecular-weight polyethylene (UHMWPE) material: An in vitro study on cell viability and interleukin-6 expression. J Pharm Bioall Sci 2018;10:43-7 |
How to cite this URL:
Anwar IB, Santoso A
, Saputra E
, Ismail R
, Jamari J
, van der Heide E
. Initial response of human bone marrow–derived stem cells after contact with ultrahigh-molecular-weight polyethylene (UHMWPE) material: An in vitro study on cell viability and interleukin-6 expression. J Pharm Bioall Sci [serial online] 2018 [cited 2021 Dec 8];10:43-7. Available from: https://www.jpbsonline.org/text.asp?2018/10/1/43/227681 |
| Introduction | |  |
Ultrahigh-molecular-weight polyethylene (UHMWPE) is a thermoplastic polymer useful in biomaterial applications; it has high biocompatibility, chemical stability, impact strength, and wear resistance.[1] UHMWPE is known to be prone to generate wear particles after long-term use in joint arthroplasty surgery.[2],[3],[4] Polyethylene debris induces inflammatory responses from macrophages, osteoclasts, osteoblasts, and fibroblasts. These cells produce cytokines that stimulate osteoclast activity and promote osteolysis.[5],[6],[7],[8],[9],[10] It was reported earlier that variation in the shape of UHMWPE particle debris could induce different cellular responses. UHMWPE debris with sharp fibular-shaped particles induced a substantial increase in cellular infiltration and increased expression of interleukin-1β (IL-1β) and tumor necrosis factor-α (TNF-α) in the murine air pouch model when compared to globular-shaped particles of a similar volume.[11] Furthermore, Sieving et al.[12] reported variation in cellular response to various shapes and surface roughness of UHMWPE particle. Their investigation suggested that both shape and surface roughness influence the severity of specific inflammatory responses, and the rough surface debris induce a marked effect on adverse tissue responses when combined with particles that have a sharp, elongated shape.[12] Although the effects of polyethylene debris to several human cells have been well studied, little is known about its cellular effect at the initial contact as a block material (non-particle debris). This study aimed to investigate the response of human bone marrow–derived stem cells to a block material of UHMWPE that resembles the initial situation when total arthroplasty prosthesis was implanted in a human joint.
| Materials and Methods | | |
Human bone marrow–derived stem cell isolation, culture, and immunohistochemistry
This study was approved by the Ethics Commission of Prof. Dr. R. Soeharso Orthopaedic Hospital, Solo, Indonesia. Approximately 10mL bone marrow suspension was harvested from the femoral intramedullary canal of patients who received total hip arthroplasty surgery after obtaining written consent. It was collected in a 20-mL tube (Falcon; BD Bioscience, Bedford, MA, USA) containing an equal volume of heparinized (10 U/mL) phosphate-buffered saline (PBS) to avoid clotting. The mixture of heparinized PBS and bone marrow was kept at 4°C before further processing. The culture processes were conducted in the Laboratory of Cell Culture at the Department of Physiology, School of Medicine, Gadjah Mada University, Yogyakarta, Indonesia.
The obtained bone marrow was loaded and centrifuged at 2500rpm for 10min at room temperature. The upper layer of mononuclear cells was collected and washed with PBS twice and with Dulbecco’s modified Eagle’s medium (DMEM) once. The isolated cells were suspended in DMEM, supplemented with 15% PBS and 1% antibiotic–antimycotic solution (Sigma-Aldrich, St. Louis, MO, USA), and seeded into 25cm2 flasks. The cells were then incubated at 37°C, 5% CO2. The nonviable cells were removed by washing twice with PBS on the third day, and new medium was applied. We used inverted microscope to evaluate the cell density and morphology. When 80% of cells confluence was reached, they were harvested using 0.25% trypsin (Sigma-Aldrich) and then subcultured. We used the third passage of cells for subsequent studies [Figure 1].  | Figure 1: Isolated hBMSC after third passage of cultivation. A more than 80% of cells confluence was obtained (10×)
Click here to view |
Immunohistochemistry staining was used for confirmation of the obtained stem cells. A 4% paraformaldehyde solution was used for fixation of the cells. It was blocked to avoid a nonspecific antibody binding. Then an overnight incubation with primary antibodies at 4°C was carried out. For specific cell evaluation, anti-CD-44 and anti-CD-19 were used for human bone marrow stem cell (hBMSC) (Bioss, Woburn, MA, USA). Mesenchymal lineage stem cells were confirmed with the positive result of CD-44 and hematopoietic lineage stem cells with that of CD-19. A fluorescence microscope (Eclipse E400; Nikon, Tokyo, Japan) was used in this process.
Cytotoxicity study of UHMWPE on hBMSC and IL-6 expression
A 96-well microplate was used for re-culture of the obtained stem cells. One 96-well microplate was prepared for each incubation period: 24, 48, and 72h. The UHMWPE implants were placed in the wells before seeding the stem cells into the wells. The implants consist of two different sizes: UHMWPE with size 2×2mm (size A) and with size 4×2mm (size B). Both of them had 1mm thickness [Figure 2]. After seeding of 1×104 cells, the plates were incubated at 37°C, 5% CO2 for 24, 48, and 72h. An inverted microscope was used for the evaluation of cells. Before the cytotoxicity study, we collected the culture medium for the measurement of IL-6 expression.  | Figure 2: UHMWPE material for in vitro cell reaction study: size A (smaller), 2×2 × 1mm; size B, 4×2 × 1 mm
Click here to view |
A 50-μL solution containing 5mg/mL of 3-(4,5-dimethylthiazol 2-yl)-2,5-diphenyltetrazolium (MTT) reagent in PBS was added to each well of 96-well microplate, which will be evaluated for cytotoxicity study, and then reincubated for 4h in 5% CO2 and 37°C. Viability of the cells was evaluated with colorimetric assay after incubation for 24, 48, and 72h with UHMWPE implant treatment. To each well, 50 μL dimethyl sulfoxide was added and reincubated for 5min at 37°C to accomplish the cytotoxicity test process. We measured the optical density of each well using enzyme-linked immunosorbent assay (ELISA) reader in 620-nm wavelength. With a significance of 95%, the data were tabulated and analyzed using t-test (version 17; SPSS, Chicago, Illinois, USA). Viable cell percentage was calculated using the IC50 formula.[13] The amount of IL-6 on culture medium was quantified by an immunoassay kit (ELISA; Koma Biotech, Yeongdeungpo-gu, Seoul, Korea).
| Results | | |
Human bone marrow–derived stem cell cultures and cytotoxicity study
Visual microscopic evaluation was carried out in all the study groups before performing MTT assay using an inverted microscope (Eclipse E400; Nikon). We found that bone marrow–derived stem cells attached to the implant in all the experiment groups [Figure 3]. According to the results of MTT assay, there was no statistical difference in the optical cell density of all treatment groups compared to control group at 24, 48, and 72h of incubation period [Table 1], [Table 2], [Table 3], [Table 4].  | Figure 3: Microscopic analysis of hBMSC around UHMWPE implants. Stem cells attached to the implant in all groups (×10). Size A, 24h (A); size B, 24h (B); size A, 48h (C); size B, 48h (D); size A, 72h (E); size B, 72h (F)
Click here to view |
 | Table 1: Mean and standard deviation of cell optical density of all study groups at 24, 48, and 72h of incubation period
Click here to view |
 | Table 2: Difference of mean optical density between incubation periods of cell control group
Click here to view |
 | Table 3: Difference of mean optical density between incubation periods of size A implant group
Click here to view |
 | Table 4: Difference of mean optical density between incubation periods of size B implant group
Click here to view |
Statistical analysis showed that at the control groups significant difference (P < 0.05) was observed between 24 and 72h group, also between 48 and 72h group. No significant difference was observed between 24- and 48-h groups. In the treatment group, significant difference was found in size A and size B implants between 48 and 72h and between 24 and 72h of incubation period, respectively. At 24, 48, and 72h, all treatment groups showed >50% cells that were viable [Table 5].  | Table 5: Percentage of stem cell viability after contact with UHMWPE after each incubation period
Click here to view |
| Expression of IL-6 | | |
According to the results of ELISA, we found lower expression of IL-6 in hBMSC compared to control group at 48h of incubation period both in size A and size B implants. We found higher IL-6 expression compared to control group at 72h of incubation period in size A implant [Figure 4].
| Discussion | | |
A study by Chiu et al.[14] evaluated the effect of UHMWPE particle on murine bone marrow osteoprogenitor cells; the study showed that UHMWPE particles inhibit the osteogenic activity of osteoprogenitor cells, which may result in reduced periprosthetic bone regeneration and repair. Exposure of both cell population to UHMWPE particles resulted in a dose-dependent decrease in mineralization, proliferation, alkaline phosphatase activity, and osteocalcin production when compared with control cells cultured on collagen matrix without particles.[14] Another study by Preedy et al.[15] reported the changes in cell elasticity and spring constant of rat mesenchymal stem cells (MSCs) exposed to wear particles occurred in the first 24h of contact. The particle concentration ranging from 0.5 to 50mg/L did not play a significant role.[13] Cell viability study by Lin et al.
[16] using cultured mouse MSCs resulted in a decrease of cell viability after contact with UHMWPE particle wear. Huang et al.[17] examined the effect of UHMWPE particle wear on chemotaxis of human MSCs. They found that chemokines released by macrophages stimulated by wear particles can have an effect on the migration of macrophages and MSCs.
Different to previously reported studies, our study involved an hBMSC response examination to a block of UHMWPE material (non-particle) resembling the real intraoperative condition when a block of UHMWPE material was implanted in a human joint during joint replacement surgery. We believe this method could explain the early cell response after contact with UHMWPE material. In our study, we found there was a decrease in cell viability at the 48-h incubation period of smaller implant; however, there was still high cells viability at 72-h incubation period. This finding was consistent with the expression of IL-6 in smaller implant group (48h), which was the lowest IL-6 expression compared to other incubation period. No modulation on IL-6 expression was seen after 24h of contact with UHMWPE material as compared to control group. IL-6 expression was downregulated at 48h of contact with UHMWPE. However, it was re-increased at 72h of incubation period. The pattern of IL-6 expression in the experiment group was different from the result in the control group.
In this study, the cell viability and IL-6 expression after contact with a larger (size B) UHMWPE material showed an inconsistent pattern. Despite stable, excellent cell viability during all incubation periods, a marked decrease of IL-6 expression was observed at the 72-h incubation period. This finding indicates that the cellular response to UHMWPE may vary with size and volume of the UHMWPE block material, and further study is needed in this regard. For comparison, Rader et al.[18] reported that the volume of UHMWPE wear particles is an important factor for the release of cytokines. Certain volume of wear particle is needed for maximum release of inflammatory mediators (TNFα, IL-1, IL-8).[18]
| Conclusions | | |
hBMSC showed a high cell viability after initial contact with UHMWPE material. Modulation of IL-6 expression was present at the initial stage as a response to foreign material.
Financial support and sponsorship
This study was funded by PUSNAS research grant of the Ministry of Research, Technology and Higher Education of Indonesia, based on the agreement letter: 022/SP2H/LT/DRPM/II/2016 on 17 February, 2016.
Conflicts of interest
There are no conflicts of interest.
| References | | |
| 1. | Onate J, Comin M, Braceras I, Garcia A, Viviente J, Brizuela M, et al. Wear reduction effect on ultra-high-molecular-weight polyethylene by application of hard coatings and ion implantation on cobalt chromium alloy, as measured in a knee wear simulation machine. Surf Coating Tech 2001;142:1056-62.  |
| 2. | Brach Del Prever EM, Bistolfi A, Bracco P, Costa L. UHMWPE for arthroplasty: Past or future? J Orthop Traumatol 2009;10:1-8. |
| 3. | Perni S, Kong MG, Prokopovich P. Cold atmospheric pressure gas plasma enhances the wear performance of ultra-high molecular weight polyethylene. Acta Biomater 2012;8:1357-65. [ PUBMED] |
| 4. | van Ooij A, Kurtz SM, Stessels F, Noten H, van Rhijn L. Polyethylene wear debris and long-term clinical failure of the Charité disc prosthesis: A study of 4 patients. Spine (Phila Pa 1976) 2007;32:223-9. |
| 5. | Wright T, Goodman SB. Implant wear in total joint replacement. (Rosemont, IL): American Academy of Orthopaedic Surgeons; 2001. |
| 6. | Vermes C, Chandrasekaran R, Jacobs JJ, Galante JO, Roebuck KA, Glant TT. The effects of particulate wear debris, cytokines, and growth factors on the functions of MG-63 osteoblasts. J Bone Joint Surg Am 2001;83A:201-11. |
| 7. | Vermes C, Roebuck KA, Chandrasekaran R, Dobai JG, Jacobs JJ, Glant TT. Particulate wear debris activates protein tyrosine kinases and nuclear factor jB, which down-regulates type I collagen synthesis in human osteoblasts. J Bone Miner Res 2000;15:1756-65. [ PUBMED] |
| 8. | Dean DD, Schwartz Z, Blanchard CR, Liu Y, Agrawal CM, Lohmann CH, et al. Ultrahigh molecular weight polyethylene particles have direct effects on proliferation, differentiation, and local factor production of MG63 osteoblast-like cells. J Orthop Res 1999;17:9-17. |
| 9. | Dean DD, Schwartz Z, Liu Y, Blanchard CR, Agrawal CM, Mabrey JD, et al. The effect of ultra-high molecular weight polyethylene wear debris on MG63 osteosarcoma cells in vitro. J Bone Joint Surg Am 1999;81:452-61. |
| 10. | Lohmann CH, Schwartz Z, Koster G, Jahn U, Buchhorn GH, MacDougall MJ, et al. Phagocytosis of wear debris by osteoblasts affects differentiation and local factor production in a manner dependent on particle composition. Biomaterials 2000;21:551-61. |
| 11. | Yang SY, Ren W, Park Y, Sieving A, Hsu S, Nasser S, et al. Diverse cellular and apoptotic responses to variant shapes of UHMWPE particles in a murine model of inflammation. Biomaterials 2002;23:3535-43. |
| 12. | Sieving A, Wu B, Mayton L, Nasser S, Wooley PH. Morphological characteristics of total joint arthroplasty-derived ultra-high molecular weight polyethylene (UHMWPE) wear debris that provoke inflammation in a murine model of inflammation. J Biomed Mater Res 2003;64A:457-64. |
| 13. | Sumarta NPM, Danudiningrat CP, Rachmat EA, Soesilawati P. Cytotoxicity difference of 316L stainless steel and titanium reconstruction plate. Dent J (Maj Ked Gigi) 2011;44: 7-11. |
| 14. | Chiu R, Ma T, Smith RL, Goodman SB. Ultrahigh molecular weight polyethylene wear debris inhibits osteoprogenitor proliferation and differentiation in vitro. J Biomed Mater Res A 2009;89:242-7. |
| 15. | Preedy EC, Perni S, Prokopovich P. Nanomechanical and surface properties of rMSCs post-exposure to CAP treated UHMWPE wear particles. Nanomedicine 2016;12:723-34. |
| 16. | Lin TH, Sato T, Barcay KB, Waters H, Loi F, Zhang R, et al. NF-kB decoy oligodeoxynucleotide enhanced osteogenesis in mesenchymal stem cells exposed to polyethylene particle. Tissue Eng Part A 2015;21:875-83. |
| 17. | Huang Z, Ma T, Ren PG, Smith RL, Goodman SB. Effects of orthopedic polymer particles on chemotaxis of macrophages and mesenchymal stem cells. J Biomed Mater Res A 2010;94:1264-9. |
| 18. | Rader CP, Sterner T, Jakob F, Schütze N, Eulert J. Cytokine response of human macrophage-like cells after contact with polyethylene and pure titanium particles. J Arthroplasty 1999;14:840-8. |
[Figure 1], [Figure 2], [Figure 3], [Figure 4]
[Table 1], [Table 2], [Table 3], [Table 4], [Table 5]
|