Fracture resistance of titanium, chrome–cobalt, and gold alloy as post and core materials: A comparative evaluation
Karunakaran Jeyaraman Venkataraman1, Sathya Thanapathi1, Sathyanarayanan Balasubramanian1, Shrimanikandan Ayappa Gandhi2, Anagha Chandrasekharan Sarojinikutty1
1 Department of Conservative Dentistry, JKK Nataraja Dental College & Hospital, Komarapalayam, Tamil Nadu, India
2 Department of Craniofacial Surgery & Dentistry, Velammal Medical Hospital & Research Institute, Madurai, Tamil Nadu, India
|Date of Submission||02-Mar-2020|
|Date of Decision||10-Mar-2020|
|Date of Acceptance||31-Mar-2020|
|Date of Web Publication||28-Aug-2020|
Karunakaran Jeyaraman Venkataraman
Department of Conservative Dentistry, JKK Nataraja Dental College & Hospital, Komarapalayam, Tamil Nadu.
Source of Support: None, Conflict of Interest: None
| Abstract|| |
Aim: This study aimed to comparatively evaluate the fracture resistance of different metallic post and core materials. Materials and Methods: Twenty-four maxillary–central incisors were selected, standardized, and segregated into three groups (GP I–III) (n = 8) based on the type of alloy used for post and core preparation. GP I (gold alloy [Au]), GP II (chrome–cobalt alloy [Co–Cr]), and GP III (titanium alloy [Ti]) were comparatively evaluated for use as post and core materials. The teeth were endodontically treated and tooth preparation for post core was done.Metal post and cores were fabricated using indirect wax pattern and luted. Teeth were mounted on resin bases, fracture testing was done, and type of fractures were analyzed. Results: Mesiodistal type of fracture was the most common among experimental groups with a percentage incidence of 54.20%. The comminuted type of fracture was the next most common with a percentage incidence of 29.2%. The incidence of buccolingual, transverse, and other type of fracture was not common and had a percentage incidence of 29.2%, 4.2%, 8.3% and 4.2% respectively. Group II had the highest fracture resistance with a mean value of 742.89N. Group III and Group I had mean values of 482.33 and 361.1123N. Statistically significant difference between experimental groups (I and II) and (II and III) was observed in load values of root fracture (P < 0.05). Conclusion: On the basis of the protocols used and limitations of this study, among metallic post and core materials tested, GP II had the highest fracture resistance values. Further evaluation of these different post and core systems, new alloy formulations designed specifically for use as post and core materials, and assessment in a clinical setting is recommended.
Keywords: Chrome-cobalt alloy, gold alloy, metallic post and core materials, post and core, post-endodontic restoration, titanium alloy
|How to cite this article:|
Venkataraman KJ, Thanapathi S, Balasubramanian S, Gandhi SA, Sarojinikutty AC. Fracture resistance of titanium, chrome–cobalt, and gold alloy as post and core materials: A comparative evaluation. J Pharm Bioall Sci 2020;12, Suppl S1:583-8
|How to cite this URL:|
Venkataraman KJ, Thanapathi S, Balasubramanian S, Gandhi SA, Sarojinikutty AC. Fracture resistance of titanium, chrome–cobalt, and gold alloy as post and core materials: A comparative evaluation. J Pharm Bioall Sci [serial online] 2020 [cited 2021 Apr 22];12, Suppl S1:583-8. Available from: https://www.jpbsonline.org/text.asp?2020/12/5/583/292852
| Introduction|| |
Excessive tooth structure removal and subsequent dehydration are responsible for affecting fracture resistance of restored tooth structure after endodontic therapy. Resistance to fracture after endodontic therapy depends primarily on remaining dentin thickness, especially in a buccolingual direction. Creation of excessive stress during obturation and use of higher concentration of irrigants with prolonged exposure times increase susceptibility of tooth to fracture, which reduces long-term survival rate, which is undesirable. Endodontic therapy should ideally reinforce the residual tooth structure. A considerable amount of radicular dentin in coronal and middle one-third is intentionally removed during biomechanical instrumentation, more so in case of curved canals, which weakens root structure.
Rotary instruments exert considerable stresses in certain portions of canal wall and form microcracks, which become areas of increased stress concentration and predisposes to root fracture. These cracks spread or extend slowly over a period to the surface, eventually resulting in root fracture. Stress concentration of radicular dentin in coronal one-third of root under lateral forces makes teeth susceptible to fracture at cementoenamel junction. The amount of remaining radicular and coronal dentin is directly proportional to fracture resistance. Single file systems have been reported to reduce the amount of stresses on canal walls. Fractures that occur post endodontic therapy can either be horizontal or vertical root fractures. Retreatment procedures also further removes dentin from within the canal rendering retreated teeth more susceptible to fracture. This study aims to comparatively analyze resistance to fracture of gold alloy (Au), chrome–cobalt (Co–Cr), and titanium alloy (Ti) post and core preparations in maxillary central incisors.
| Materials and Methods|| |
Extracted permanent maxillary central incisors were cleansed, and analyzed using radiovisiography. Twenty-four teeth with mature, intact root apices were selected. Mesiodistal and buccolingual diameters at the level of cementoenamel junction were tabulated with digital vernier calipers. Samples were weighed using precision weighing scale, tested for normality, and were evenly distributed across three experimental groups (n = 8) and stored (4°C, normal saline) [Figure 1].
Access was done and 15K-file (Dentsply Maillefer, Ballaigues, Switzerland) was inserted passively in canal until tip was visualized and adjusted to apical foramen. Working length was calculated by subtracting 0.5 mm from the recorded value, and canal preparation was done to master apical file size 40 using hand files (step-back preparation). A 3% sodium hypochlorite (8 mL) as initial and 17% ethylenediaminetetraacetic acid (EDTA) (5 mL/3 min) final were used for irrigation. A post-final rinse of 5 mL of distilled water was done.
Obturation was done by cold lateral condensation, and samples were stored at 37°C at 100% relative humidity for 72h. Teeth were decoronated 3 mm from the deepest point of cementoenamel junction by comparing mesial and distal surfaces using a digital vernier caliper. Gutta-percha from canal was removed using Touch N Heat device (SybronEndo Orange, CA, USA), walls were cleared of sealer using Hedstrom files and size-1 Peeso reamer with care not to remove radicular dentin. A minimum apical seal of 5 mm was retained. Samples were assessed using radiovisiography for consistent finish and gutta-percha removal from canal.
Crown preparation was done using TF–12 flat-end tapered fissure bur (SS White burs) with a tip diameter of 1 mm, core ferrule was given using thin-tapered fissure burs. An anti-rotation notch was given for a depth of approximately 2 mm using flat-end tapered fissure bur on the thickest portion of root. Core height of all samples was standardized to 3 mm. Apical end of the post space preparation was assessed, gauged, and standardized to a specific width. The walls were cleansed, sealed with cotton plugs, and stored. Group I post and core wax pattern was fabricated using stainless steel sprue former (18g) with medium inlay wax (dental inlay casting wax, ). Subsequently after debubblizing and investing, pattern was cast (BEGO induction casting machine) with Au (20 carats) using a lost wax technique. In Group II, direct technique was used to fabricate post and core wax pattern using prepared sprue former (18g) with a modeling wax (Geo Crowax; Renfert, Hilfingen, Germany). After debubblizing and investing, casting was done (BEGO induction casting machine, BEGO Bremer Goldschlägerei Wilh. Herbst GmbH & Co. KG, Bremen, Germany) with Co–Cr (Colado CC, Ivoclar Vivadent, AG, Principality of Liechtenstein) using lost wax technique. In Group III, root canal impressions obtained using direct wax patterns were scanned with digital scanner and a three-dimensional image was generated. Post and core was then fabricated using a laser sintering process for Ti (SISMA MYSINT 100, laser metal fusion).
Samples from each group were mounted on base (1.5” × 1.5” × 1.5”) vertically at an angle of 30° to long axis, clear epoxy resin was poured and allowed to set for 72h and coded. They were kept covered by moist cotton till fracture testing. Samples were tested with the help of universal testing machine using a custom metal indenter (3 mm) with a crosshead speed of 1 mm/min, and the results were recorded.
Fracture types were observed, grouped, and recorded. The results were assessed by two different operators, compared, and tabulated. The samples were distributed across groups based on their weights and homogenicity. They were statistically assessed for normality of these variables. The results of fracture test were statistically analyzed using one-way analysis of variance (ANOVA) test of variance with Tukey post hoc test for multiple comparisons.
| Results|| |
Group II had the highest fracture resistance with a mean value of 742.89 N. Groups III and I had mean values of 482.33 and 361.1123 N, respectively. Statistically significant difference between the experimental groups (I and II) and (II and III) in load values of root fracture (P < 0.05) [Figure 2][Figure 3][Figure 4][Figure 5] was observed.
Mesiodistal type of fracture was the most common among experimental groups with a percentage incidence of 54.20%. The incidence of comminuted, buccolingual, transverse, and other type of fractures were 29.2%, 4.2%, 8.3%, and 4.2%, respectively [Figure 6][Figure 7][Figure 8].
| Discussion|| |
Endodontic therapy should reinforce residual tooth structure in a way that it prevents untoward events long term. To effectively access and prepare apical one-third, considerable amount of radicular dentin in coronal and middle one-third is removed. Factors affecting fracture susceptibility are tooth structure loss, trauma, age, tooth type, degree of calcification, excessive dentin removal, dehydration of dentin subsequent to endodontic therapy, obturation-induced stresses, and irrigant action on canal walls, which reduces long-term survival rate. Root thickness and ability to resist lateral dislodging forces have a directly proportional relationship. Fracture resistance improves with increase in the remaining root dentin thickness buccolingually.
Vertical fractures can happen before, during, or after endodontic therapy. Roots are split along their long axis in vertical fracture and rarely occur as a result of acute trauma. Clinical studies revealed that 11%–13% of extracted teeth after endodontic treatment have been associated with vertical fractures and most often have unfavorable prognosis. Craze lines and cracks on canal walls become areas of high stress concentration and over a period extend to surface eventually, resulting in vertical root fracture. Cracks usually begin at the apex of root and propagate at the cervical.
Horizontal fractures are the most common, and they occur mainly in the anterior region due to frontal impact. They are common in middle one-third and rarely occur in apical and coronal one-third of root. Successful management of transverse root fracture depends on fracture line position, mobility of coronal segment, status of radicular, and coronal pulp tissues. Prognosis for teeth with transverse or horizontal root fractures is usually good. Verified pulp necrosis has been reported with a percentage incidence of 43.7%, and the treatment depends on the position of tooth after it was fractured, the mobility of coronal segment, the status of the pulp, and the position of fracture line. Repair and healing occurs either by hard tissue union, which is a desirable, bony ingrowth, fibrous healing, or granulation tissue formation. Fractures as a result of fatigue due to repetitive occlusal forces have been reported in teeth, which are vital. The position and relationship of fracture line to gingival crevice is the most important factor, affecting the long-term prognosis. Coronal and middle one-third fractures have less favorable prognosis compared to apical root fractures. In infrabony fractures with no communication to gingival sulcus, meticulous oral hygiene and appropriate treatment options result in successful outcomes.
Rotary files used for gutta-percha removal during retreatment have been shown to remove surface dentin. Further enlargement of apical third to achieve better cleansing contributes to reduced fracture resistance. There has been a positive correlation between the removal of dentin during retreatment procedures and the reduction of fracture resistance.
Newer generation of materials improve bond between radicular dentin, sealer, and sealer–core interface, which improves fracture resistance. Modulus of elasticity of obturation material should ideally be approximate to that of radicular dentin for root reinforcement. Priming radicular dentinal surface improves bond between sealer, dentin, and core. Also the modulus of elasticity of obturating material, post, and sealer has to match that of radicular dentin, leading to even distribution of induced stresses, and borne by components of monoblock.
Failure rates were almost double where adequate post-endodontic restoration was not done. Use of intra-orifice barriers effectively decreases coronal leakage and improves fracture resistance., Cast post and core preparation removes radicular dentin, needs multiple clinical visits, leading to more turnover time, and has an elastic modulus, which is high (200 Gpa) compared to tooth structure, which can predispose to fractures. Metallic post failures are most often due to root fracture, post-fracture, or post-retention loss. In endodontically treated teeth, the amount of remaining dentin and the provision of ferrule increase survival rate. Studies with longer follow-up have been recommended.
Endodontic irrigation leads to an alteration of chemical composition, organic and inorganic phases of radicular dentin, which affects microhardness, permeability, and solubility leading to changes in the ability of teeth to resist fracture under varying loads. EDTA affects fracture resistance based on the exposure time and concentration.
Sealers contributing to improving fracture strength of the roots have been evaluated. Adhesion to canal walls increases mechanical interlocking and reduces risk of fracture. Obturation material and technique choices impact the resistance of root to fracture. Gutta-percha along with adhesive resin sealers have been reported to improve the fracture resistance. Adhesive ionomer coating on gutta-percha for a thickness of 2 microns to which a adhesive ceramic sealer could be bonded to form a tertiary monoblock improves facture resistance.
Gutta-percha used with a resin-based sealer has several advantages but its hydrophobic nature and its inability to sufficiently reinforce the root have fuelled the development of hydrophilic materials, which penetrate dentinal tubules and use moisture in dentinal walls, which allows the material to bond to root canal wall and core, which reinforces the root. Polymerization shrinkage of the resin-based sealers due to high C-factor associated with root canal results in sealer contraction post filling and weakening bond between sealer and canal wall, leading to reduced resistance to fracture. A novel sealer, which has the property of sealer expansion, due to its self-expanding and hydrophilic composition significantly increased the resistance to fracture.
There has been a positive correlation between the microcrack formation and the incidence of root fractures. Root fracture is a gradual propagation of craze lines and microcracks in radicular dentin. Microcracks are formed as a result of rotational forces that are being applied to canal walls. Increased incidence, reported with some rotary instrumentation techniques, is related to design features of rotary instruments such as tip size, cross-sectional geometry, pitch, and taper. Hand instruments produce a less dentinal defects compared to rotary instruments. Investigators have found a proportional relationship between rotary instrument design and vertical fractures. Migration from a rotary to reciprocating motion, involving different clockwise, counter-clockwise angles, results in minimal torsional, flexural stresses, and less radicular dentin binding. Reciprocating file systems produce significant amount of incomplete dentinal cracks in apical third when compared to rotary files. Both hand and reciprocating instruments induced the formation of dentinal defects during the canal preparation. Self-adjusting file drastically changes the way in which canal is prepared. Straightening of curved canals is reduced because of the absence of a rigid core and pliability of file. The file removes a surface layer of dentin, which results in a canal of larger dimensions but a similar cross section.
Cracks or craze lines that extend from external surface of root into dentin, which do not reach the root canal lumen and structural defects in root dentin, have been found to cause fractures due to amplification of induced stresses at these formed microcracks. They were found in areas away from direct contact of rotary instruments. One possible reason is that stress generated during instrumentation of canals is transmitted to external surface of teeth where it overcomes bonds in dentin to form these craze lines, microcracks, and eventually resulting in fractures.,
This in vitro study evaluated the fracture strength on extracted maxillary central incisors, and due to large amount of variations in volume and weight of roots among the samples selected, sufficient protocols were followed for the standardization of controllable factors. Normality testing of these variables was assessed statistically, and distributions were found to be normal at 5% level of significance.
| Conclusion|| |
Radicular dentin should be preserved as much as possible during endodontic therapy. The choice of instrumentation protocols followed, obturating technique, and the choice of materials has to be customized to individual tooth based on preoperative analysis, which would lead to better long-term outcomes. Metallic post and core preparations seem an attractive option. Development of newer alloy systems and materials, which are biocompatible and match elastic modulus of dentin, are recommended.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Robbins JW Restoration of the endodontically treated tooth. Dent Clin North Am 2002;46:367-84.
Sedgley CM, Messer HH Are endodontically treated teeth more brittle? J Endod 1992;18:332-5.
Sornkul E, Stannard JG Strength of roots before and after endodontic treatment and restoration. J Endod 1992;18:440-3.
Yoldas O, Yilmas S, Atakan G, Knudsen C, Kasan Z Dentinal microcrack formation during root canal preparations by different rotary NiTi instruments and the self-adjusting file. J Endod 2012;38:232-5.
Lertchirakarn V, Timyam A, Messer HH Effects of root canal sealers on vertical root fracture resistance of endodontically treated teeth. J Endod 2002;28:217-9.
Metzger Z, Teperovich E, Zary R, Cohen R, Hof R The self-adjusting file (SAF). Part 1: respecting the root canal anatomy—a new concept of endodontic files and its implementation. J Endod 2010;36:679-90.
Johnson ME, Stewart GP, Nielsen CJ, Hatton JF Evaluation of root reinforcement of endodontically treated teeth. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2000;90:360-4.
Fuss Z, Lustig J, Tamse A Prevalence of vertical root fractures in extracted endodontically treated teeth. Int Endod J 1999;32:283-6.
Meister F Jr, Lommel TJ, Gerstein H Diagnosis and possible causes of vertical root fractures. Oral Surg Oral Med Oral Pathol 1980;49:243-53.
Lo Giudice R, Lizio A, Cervino G, Fabiana N, Francesco P, Ausiello P, et al
. The horizontal root fractures. Diagnosis, clinical management and three-year follow-up. Open Dent J 2018;12:687-95.
Al-Nazhan S, Andreasen JO, Al-Bawardi S, Al-Rouq S Evaluation of the effect of delayed management of traumatized permanent teeth. J Endod 1995;21:391-3.
Ganesh A, Venkatesh Babu N, John A, Deenadhayalan G, Kandaswamy DA Comparative assessment of fracture resistance of endodontically treated and retreated teeth: an in-vitro
study. J Cons Dent 2014;17:61-5.
Williams C, Loushine RJ, Weller RN, Pashley DH, Tay FR A comparison of cohesive strength and stiffness of resilon and gutta-percha. J Endod 2006;32:553-5.
Tay FR, Pashley DH Monoblocks in root canals: a hypothetical or a tangible goal. J Endod 2007;33:391-8.
Swartz DB, Skidmore AE, Griffin JA Twenty years of endodontic success and failures. J Endod 1983;9:198-202.
Yavari HR, Samiei M, Shahi S, Aghazadeh M, Jafari F, Abdolrahimi M, et al
. Microleakage comparison of four dental materials as intra-orifice barriers in endodontically treated teeth. Iran Endod J 2012;7:25-30.
Roghanizad N, Jones JJ Evaluation of coronal microleakage after endodontic treatment. J Endod 1996;22:471-3.
Sarkis-Onofre R, Skupien JA, Cenci MS, Moraes RR, Pereira-Cenci T The role of resin cement on bond strength of glass-fiber posts luted into root canals: a systematic review and meta-analysis of in vitro
studies. Oper Dent 2014;39: E31-44.
Marchionatti AME, Wandscher VF, Rippe MP, Kaizer OB, Valandro LF Clinical performance and failure modes of pulpless teeth restored with posts: a systematic review. Braz Oral Res 2017;31:e64.
Uzunoglu E, Aktemur S, Uyanik MO, Durmaz V, Nagas E Effect of ethylenediaminetetraacetic acid on root fracture with respect to concentration at different time exposures. J Endod 2012;38:1110-3.
Bhat SS, Hegde SK, Rao A, Mohammed SAK Evaluation of resistance of teeth subjected to fracture after endodontic treatment using different root canal sealers: an in-vitro
study. J Indian Soc Pedod Preventive Dent 2012;4:305-9.
Jhamb S, Nikhil V, Singh V Effect of sealers on fracture resistance of endodontically treated teeth with and without smear layer removal: an in vitro
study. J Conserv Dent 2009;12:114-7.
Sandikci T, Kaptan RF Comparative evaluation of the fracture resistances of endodontically treated teeth filled using five different root canal filling systems. Niger J Clin Pract 2014;17:667-72.
Celikten B, Uzuntas CF, Gulsahi K Resistance to fracture of dental roots obturated with different materials. Biomed Res Int 2015;2015:591031.
Hegde V, Arora S Fracture resistance of roots obturated with novel hydrophilic obturation systems. J Conserv Dent 2015;18:261-4.
Bolla M, Muller-Bolla M, Borg C, Lupi-Pegurier L, Laplanche O, Leforestier E WITHDRAWN: root canal posts for the restoration of root filled teeth. Cochrane Database Syst Rev 2016;11:CD004623.
Shori DD, Shenoi PR, Baig AR, Kubde R, Makade C, Pandey S Stereomicroscopic evaluation of dentinal defects induced by new rotary system: “protaper NEXT”. J Conserv Dent 2015;18:210-3.
Kim HC, Lee MH, Yum J, Versluis A, Lee CJ, Kim BM Potential relationship between design of nickel-titanium rotary instruments and vertical root fracture. J Endod 2010;36:1195-9.
Bürklein S, Tsotsis P, Schäfer E Incidence of dentinal defects after root canal preparation: reciprocating versus rotary instrumentation. J Endod 2013;39:501-4.
Helvacioglu-Yigit D, Aydemir S, Yilmaz A Evaluation of dentinal defect formation after root canal preparation with two reciprocating systems and hand instruments: an in-vitro
study. Biotechnol Equip 2015;29:368-73.
Hof R, Perevalov V, Eltanani M, Zary R, Metzger Z The self-adjusting file (SAF). Part 2: mechanical analysis. J Endod 2010;36:691-6.
Gudoutos EE Fracture mechanics: an introduction. 2nd ed. Dordrecht, The Netherlands: Springer Publishers; 2005. pp. 79-94.
Shemesh H, van Soest G, Wu MK, Wesselink PR Diagnosis of vertical root fractures with optical coherence tomography. J Endod 2008;34:739-42.
Shemesh H, Wesselink PR, Wu MK Incidence of dentinal defects after root canal filling procedures. Int Endod J 2010;43:995-1000.
[Figure 1], [Figure 2], [Figure 3], [Figure 4], [Figure 5], [Figure 6], [Figure 7], [Figure 8]